austempering是什麼意思，austempering的意思翻譯、用法、同義詞、例句

常用詞典

n. 等溫淬火；沃斯回火法

The hardness data of quenched steel under different conditions were collected utilizing austempering tests.

利用等溫回火實驗，采集了淬火鋼在不同條件下回火時的硬度數據。

These processes, known as austempering and martempering, result in products having certain desirable physical properties.

這兩種分别被稱為奧氏體回火和馬氏體回火的工藝，能使産品具有特定所需的物理性能。

The affecting rule of alloy elements on the amounts of retained austenite in austempering transformation was also stu***d.

還探讨了合金元素對等溫轉變過程中殘留奧氏體量的影響規律。

In this paper, the influence of austempering heat treatment parameters on the microstructure and properties of ADI was stu***d.

研究了等淬工藝參數對等淬球鐵顯微組織與力學性能的影響。

The influence of austempering treatment on the microstructure, retained austenite and fracture toughness of high silicon cast steel has been stu***d.

研究了在不同等溫淬火溫度熱處理後高矽鑄鋼的顯微組織與殘餘奧氏體量和材料斷裂韌性間的關系。

n.|isothermal quenching/marquench;等溫淬火；沃斯回火法

austempering（等溫淬火）是一種特殊的熱處理工藝，主要用于鋼件，旨在獲得高強度和高韌性的貝氏體組織，同時減少傳統淬火導緻的變形和開裂風險。其核心過程包含兩個關鍵步驟：

奧氏體化與快速冷卻
将鋼件加熱至奧氏體化溫度（通常為 Ac₃ 以上 30–50°C），保溫後迅速淬入溫度介于貝氏體轉變區（約 260–400°C）的熔鹽浴或金屬浴中。
等溫保持與貝氏體轉變
在等溫槽中保持足夠時間，使奧氏體完全轉變為貝氏體（一種由鐵素體和碳化物組成的非層狀組織）。此過程避免馬氏體形成，最終空冷至室溫。

核心優勢：

典型應用：

彈簧、齒輪、軸承等高應力部件，尤其適用于中高碳鋼和合金鋼（如 SAE 4140, 5160）。

權威參考資料：

ASM International《熱處理指南》（ASM Handbook Vol. 4: Heat Treating），詳述工藝原理與參數設計。
Davenport, E. S. & Bain, E. C. 的經典研究（Transactions of AIME, 1930），首次定義貝氏體轉變動力學。
SAE International 技術報告（如 SAE J406），規範合金鋼的等溫淬火實踐。
Heat Treating Society 技術文獻，收錄工業案例與性能對比數據。

Austempering（等溫淬火/奧氏體回火）是一種金屬熱處理工藝，主要用于鋼或鑄鐵材料，通過控制溫度和時間優化材料的機械性能。以下是詳細解釋：

核心步驟：将材料加熱至奧氏體化溫度後，迅速冷卻至貝氏體轉變溫度區間（通常為250-400°C），并在該溫度下保溫一定時間，使奧氏體直接轉變為貝氏體組織，隨後空冷至室溫。
與傳統淬火的區别：傳統淬火需快速冷卻至馬氏體形成溫度，再通過回火調整性能；而等溫淬火通過單一等溫步驟完成組織轉變，減少變形和開裂風險。

如需更深入的技術細節（如具體溫度參數或工業案例），可參考材料工程專業文獻或熱處理手冊。