shrinkage porosity是什么意思，shrinkage porosity的意思翻译、用法、同义词、例句

常用词典

收缩气孔巢

The reasons resulting in the shrinkage porosity, gas-hole and impacted sand in bronze castings were analyzed.

分析了锡青铜叶轮铸件出现的缩孔、气孔、冲砂等缺陷的原因。

There easily exists shrinkage porosity due to superheat of ingate root in large plain parts investment casting.

大平面铸件常在内浇道根部出现过热，在该处产生缩松缺陷。

Shrinkage and shrinkage porosity, stress and deformation often occurs during the production of heavy steel casting.

大型铸钢件在实际生产中易产生缩孔缩松、应力变形等缺陷。

And the shrinkage porosity distribution in the castings and the mechanical properties of the castings were also researched.

研究了铸件中的缩松和铸件力学性能分布特点。

The common defects of the housing casting include cracks, sand drop, slag inclusion, shrinkage porosity and rough grain, etc.

机架的常见缺陷有裂纹、掉砂、夹渣、缩孔缩松和晶粒粗大等。

Shrinkage Porosity是材料科学与工程领域的专业术语，描述材料在凝固或冷却过程中因体积收缩形成的内部孔隙缺陷。这一现象常见于金属铸造、塑料成型等工艺中，对材料的机械性能和耐久性有显著影响。

定义与机理
Shrinkage（收缩）指材料相变（如液态转固态）时体积减小的自然现象。当收缩过程中液态补缩不足时，会形成孔隙（Porosity），即Shrinkage Porosity。例如，金属铸造中，铸件外部先凝固而内部仍为液态，若无法及时补充收缩空间，内部会形成孔洞。
影响因素
主要与材料热收缩率、冷却速率及工艺设计相关。高收缩率的合金（如铝合金）更易产生此类缺陷。NASA技术文档指出，铸造过程中温度梯度过大或浇注系统设计不合理会加剧孔隙形成。
检测与影响
工业中常用X射线断层扫描（CT）或超声波检测孔隙。孔隙会降低材料强度，尤其在航空航天领域，可能引发疲劳裂纹。研究显示，孔隙率每增加1%，铝合金的拉伸强度可下降5%-10%。
应用领域
该术语广泛用于铸造、焊接、增材制造（3D打印）等质量控制场景。例如，国际铸造杂志（International Journal of Metalcasting）多篇论文探讨了通过优化浇注温度减少收缩孔隙的方法。

“Shrinkage porosity”是一个材料科学和工程领域的专业术语，由shrinkage（收缩）和porosity（多孔性）组合而成，具体含义如下：

Shrinkage porosity 特指材料在收缩过程中形成的孔隙缺陷。常见于铸造、冶金等领域，例如：

发音：英式 [ˈʃrɪŋkɪdʒ pɔ:ˈrɒsɪti]，美式 [ˈʃrɪŋkɪdʒ pəˈrɑsɪti] 。
如需进一步了解铸造工艺或孔隙率检测方法，可参考、5、6等来源。