temper brittleness是什麼意思，temper brittleness的意思翻譯、用法、同義詞、例句

常用詞典

回火脆性

例句

However, a temper brittleness has appeared after high temper.

空冷後高溫回火産生回火脆性。

The temper brittleness of T23 steel was stu***d through heat treatment experiment.

通過熱處理試驗對t 23鋼的回火脆性進行了研究。

The fracture is brittle fracture, and the reason is that material of forming ***s takes place the temper brittleness.

引起脆性斷裂的原因是成型模産生了回火脆性。

The result showed that the reason of fracture was the temper brittleness of material. In order to avoiding the fracture, the improving method was proposed.

結果表明，螺栓斷裂原因是因材料發生回火脆性，提出了改進方法，從而杜絕了類似情況的發生。

The residual deleterious elements in steel lead to products occurring red brittleness surface crack and temper brittleness, and lead to hot strength of heat resistant steel decreasing.

鋼中的殘餘有害元素緻使鋼材産生紅脆性表面裂紋和具有回火脆性傾向，并使耐熱鋼的熱強性降低。

專業解析

“temper brittleness”（回火脆性）是材料科學中描述金屬材料在特定回火溫度下韌性顯著下降的現象。其本質是材料内部微觀結構變化導緻的脆化，通常發生在250℃至400℃（低溫回火脆性）或450℃至550℃（高溫回火脆性）兩個溫度區間。這種現象會顯著降低材料的抗沖擊性能，對機械零件和工程結構的安全性構成威脅。

機制與影響因素

雜質偏聚理論：磷、錫等雜質元素在晶界處偏聚，弱化晶界結合力（ASM International《Metals Handbook》）。
碳化物析出：回火過程中碳化物沿晶界析出，形成脆性斷裂路徑（Springer《Engineering Materials》）。
合金元素作用：鉻、錳等元素會擴大脆性溫度區間，而钼可抑制脆性（中國知網《金屬熱處理學報》）。

工業預防措施

采用快速冷卻工藝跳過脆性溫度區
添加0.2%-0.5%钼元素改善抗脆性
控制原材料中磷含量≤0.015%

該現象在核電壓力容器、航空齒輪等關鍵部件制造中需重點關注，相關研究被納入GB/T 13320-2007《鋼質模鍛件金相組織評級圖》标準檢測體系。

網絡擴展資料

“Temper brittleness”是材料科學和冶金工程領域的專業術語，中文譯為回火脆性，指淬火鋼在特定溫度範圍内回火後出現的韌性顯著下降現象。以下是詳細解釋：

定義與分類

基本概念
回火脆性表現為鋼在回火過程中，雖然硬度和強度降低，但沖擊韌性（抗斷裂能力）反而下降。這種現象與回火溫度密切相關，通常分為兩類：
- 第一類回火脆性（低溫回火脆性）：發生在200–400℃，具有不可逆性，與回火後的冷卻速度無關，斷口呈沿晶脆性特征。
- 第二類回火脆性（高溫回火脆性）：發生在450–650℃，可通過快速冷卻部分避免，具有可逆性，常由雜質元素（如磷、錫）在晶界偏聚引起。

特征與機制

微觀機制：
第一類脆性與碳化物析出和晶界弱化有關；第二類脆性則與雜質元素在緩慢冷卻時向晶界擴散有關。
表現影響：
材料脆性增加可能導緻突然斷裂，尤其在低溫或沖擊載荷下風險更高。

應用與應對

工業意義：回火脆性限制了鋼材在高溫或複雜應力環境下的使用，需通過成分優化（如添加钼）或控制冷卻速度來減輕。
術語關聯：英文中“temper”在此指回火工藝（金屬熱處理），而非情緒含義；“brittleness”強調材料脆性。

如需進一步了解具體案例或實驗數據，可參考材料科學教材或專業文獻（如搜狗百科）。