temper brittleness是什么意思，temper brittleness的意思翻译、用法、同义词、例句

常用词典

回火脆性

例句

However, a temper brittleness has appeared after high temper.

空冷后高温回火产生回火脆性。

The temper brittleness of T23 steel was stu***d through heat treatment experiment.

通过热处理试验对t 23钢的回火脆性进行了研究。

The fracture is brittle fracture, and the reason is that material of forming ***s takes place the temper brittleness.

引起脆性断裂的原因是成型模产生了回火脆性。

The result showed that the reason of fracture was the temper brittleness of material. In order to avoiding the fracture, the improving method was proposed.

结果表明，螺栓断裂原因是因材料发生回火脆性，提出了改进方法，从而杜绝了类似情况的发生。

The residual deleterious elements in steel lead to products occurring red brittleness surface crack and temper brittleness, and lead to hot strength of heat resistant steel decreasing.

钢中的残余有害元素致使钢材产生红脆性表面裂纹和具有回火脆性倾向，并使耐热钢的热强性降低。

专业解析

“temper brittleness”（回火脆性）是材料科学中描述金属材料在特定回火温度下韧性显著下降的现象。其本质是材料内部微观结构变化导致的脆化，通常发生在250℃至400℃（低温回火脆性）或450℃至550℃（高温回火脆性）两个温度区间。这种现象会显著降低材料的抗冲击性能，对机械零件和工程结构的安全性构成威胁。

机制与影响因素

杂质偏聚理论：磷、锡等杂质元素在晶界处偏聚，弱化晶界结合力（ASM International《Metals Handbook》）。
碳化物析出：回火过程中碳化物沿晶界析出，形成脆性断裂路径（Springer《Engineering Materials》）。
合金元素作用：铬、锰等元素会扩大脆性温度区间，而钼可抑制脆性（中国知网《金属热处理学报》）。

工业预防措施

采用快速冷却工艺跳过脆性温度区
添加0.2%-0.5%钼元素改善抗脆性
控制原材料中磷含量≤0.015%

该现象在核电压力容器、航空齿轮等关键部件制造中需重点关注，相关研究被纳入GB/T 13320-2007《钢质模锻件金相组织评级图》标准检测体系。

网络扩展资料

“Temper brittleness”是材料科学和冶金工程领域的专业术语，中文译为回火脆性，指淬火钢在特定温度范围内回火后出现的韧性显著下降现象。以下是详细解释：

定义与分类

基本概念
回火脆性表现为钢在回火过程中，虽然硬度和强度降低，但冲击韧性（抗断裂能力）反而下降。这种现象与回火温度密切相关，通常分为两类：
- 第一类回火脆性（低温回火脆性）：发生在200–400℃，具有不可逆性，与回火后的冷却速度无关，断口呈沿晶脆性特征。
- 第二类回火脆性（高温回火脆性）：发生在450–650℃，可通过快速冷却部分避免，具有可逆性，常由杂质元素（如磷、锡）在晶界偏聚引起。

特征与机制

微观机制：
第一类脆性与碳化物析出和晶界弱化有关；第二类脆性则与杂质元素在缓慢冷却时向晶界扩散有关。
表现影响：
材料脆性增加可能导致突然断裂，尤其在低温或冲击载荷下风险更高。

应用与应对

工业意义：回火脆性限制了钢材在高温或复杂应力环境下的使用，需通过成分优化（如添加钼）或控制冷却速度来减轻。
术语关联：英文中“temper”在此指回火工艺（金属热处理），而非情绪含义；“brittleness”强调材料脆性。

如需进一步了解具体案例或实验数据，可参考材料科学教材或专业文献（如搜狗百科）。