橫裂；[木] 橫向裂縫
Being a more serious defect, transverse crack on slab surface is very harmful to slab production and quality.
鑄坯表面橫向裂紋是連鑄坯較嚴重的缺陷，其對鑄坯的生産和質量危害很大。
The stability of the periodic motion decreases as the depth of the transverse crack on the rotating shaft increases.
裂紋深度的加大降低了系統周期運動的穩定性。
Though this text is the research on the transverse crack in the crankshaft, but the method and the conclusion should have reference value to other scholars.
本文雖然研究的是曲軸上的橫向裂紋，但是研究所采用的方法和所得出的結論對其他的學者的研究應該是參考價值的。
The transverse crack is one of the most serious defects in the continuous casting slab and it has much greater adverse influence on the quality of the CC slab.
鑄坯上的橫裂紋是連鑄闆坯上較嚴重的缺陷之一，對鑄坯質量影響較大。
Main research content including: 1 Have stu***d a same diameter shaft, study how to make use of the change of natural frequency to discern the transverse crack.
本文主要的研究内容包括：1以最簡單的等直徑光軸為例，研究了利用固有頻率的變化來識别光軸上橫向裂紋的可行性。
橫向裂紋（transverse crack）是工程材料學和結構力學中的專業術語，指沿着物體橫截面方向延伸的線性斷裂缺陷。這類裂紋通常與材料承受的應力方向垂直，常見于金屬構件、混凝土結構或複合材料中。
根據美國材料與試驗協會（ASTM E1823）的定義，橫向裂紋的形成主要與三個因素相關：①循環載荷導緻的疲勞斷裂，例如鐵軌或機械軸在反複受力後産生的橫向裂紋；②材料内部殘餘應力釋放，常見于焊接接頭的熱影響區；③環境因素引發的應力腐蝕，如橋梁鋼索在潮濕含氯環境中的開裂。
英國結構工程師學會（Institution of Structural Engineers）的技術報告指出，在混凝土結構中，橫向裂紋多由幹縮應變或溫度梯度引起，其寬度超過0.3mm即會影響結構耐久性。通過超聲波探傷、數字圖像相關（DIC）等技術可進行非破壞檢測。
材料科學領域研究顯示，金屬材料的橫向裂紋擴展速度遵循Paris定律公式： $$ frac{da}{dN} = C(Delta K)^m $$ 其中$a$為裂紋長度，$N$為載荷循環次數，$Delta K$為應力強度因子幅值。該公式被廣泛應用于航空發動機葉片等關鍵部件的壽命預測。
"transverse crack" 是一個結合了“transverse”（橫向的）和“crack”（裂紋）的術語，通常用于工程、材料科學或機械領域。以下是詳細解釋：
如需進一步了解具體領域（如材料力學）的公式或案例，可補充說明需求。