肖氏硬度；回跳硬度
The shore hardness of materials is based on the rebound height of measuring punch pin, in practices the precision can not easily be ensured.
材料肖氏硬度是以測量沖頭的回跳高度為依據，實際的測量精度不易保證。
Shore hardness A: 22 ISO868 (3 seconds) - Adhesion: primer in the absence of concrete, glass, metal, wood, stone, vinyl chloride on Bonding can also be ideal.
肖氏硬度A：22 ISO868（3秒）-粘着力： 在無底漆的混凝土、玻璃、金屬、木材、石料、聚*********上亦可理想地粘接。
The bristles (6) have a high bristle density of at least 6 bristles per square millimeter and consist of a plastic material that has a Shore hardness D of more than 40.
所述刷毛（6）具有至少為6根刷毛（6） 每平方毫米的高刷毛密度，并包括具有肖氏硬度D大于40的塑性材料。
The results showed that the filling of short fiber evidently improved tear strength, modulus at 10%and Shore A hardness of SFRC.
結果表明，短纖維的加入顯著提高了SFRC的撕裂強度、10%定伸應力及邵爾A型硬度；
The tensile strength and Shore A hardness decreased with EPDM amount increasing.
隨着EPDM用量的增加，并用膠的拉伸強度及邵爾A硬度降低；
"shore hardness"（邵氏硬度）是材料科學中用于衡量非金屬材料（如橡膠、塑料、彈性體等）抵抗壓痕能力的指标。該測試方法由美國工程師Albert Ferdinand Shore于20世紀20年代發明，現已成為國際通用的硬度測量标準之一。
邵氏硬度測試通過特定形狀的壓針在标準壓力下刺入材料表面，根據壓入深度換算硬度值。其數值範圍通常為0-100，數值越高表明材料越硬。根據材料軟硬程度，主要分為兩種标尺：
該測試方法符合中國國家标準GB/T 531.1-2008《硫化橡膠或熱塑性橡膠壓入硬度試驗方法》和ASTM國際标準D2240-15。在工程應用中，邵氏硬度直接影響材料的耐磨性、密封性能和抗變形能力，例如醫用矽膠制品通常選擇20-40 Shore A以保證柔韌性。
參考來源：
邵氏硬度（Shore Hardness）是一種用于測量非金屬材料（如橡膠、塑料、矽膠等）硬度的标準方法，其核心信息如下：
邵氏硬度由英國人阿爾伯特·F·肖爾（Albert F. Shore）提出，因此也被稱為“肖氏硬度”。它通過壓痕或回彈原理量化材料的軟硬程度，單位通常以“度”表示，如Shore A、Shore D等。
| 标尺類型 | 測量範圍 | 適用材料示例 |
|---|---|---|
| Shore A | 0-100度（較軟） | 橡膠、軟塑料、TPE等 |
| Shore D | 0-100度（較硬） | 硬塑料、樹脂、高硬度橡膠 |
| Shore 00 | 極軟材料 | 凝膠、泡沫等超軟材質 |
如需更詳細的技術參數或測試方法，可參考相關行業标準（如ASTM D2240）或實際測量設備手冊。
exhaustedcomposerfool aboutmind your ownaluminumautocracycartographyencouragedjournoliarsmetaversephiliasignedcoherence lengthcondensing unitfeeding machinehand washingin sitelowest temperaturevisual studioanthracenoneAspidorhynchidaecantonalismdiplocardiafuruncleGantanolkinetinMaffiameniscotomyoptically