The hydration degree of cements, the pore structure and the pore size distribution of hydrated cement mortars were analyzed by chemical binding water and mercury intrusion porosimetry(MIP).
用結合水法、壓汞法對水泥水化程度、水泥石孔結構及其分布進行研究。
The cement soil improvement principle is the cement distributes in the soil constitutes the firm core, forms the hydrated cement in all crevices the skeleton, in order to the restraint soil particles.
水泥土改良的原理是水泥分布在土中構成堅固的核心，在所有的空隙中形成水化水泥的骨架，借以約束土粒。
The effect of slag, fly ash, and calcined shale on setting time, compressive strength, resistivity, composition and microstructure of hydrated product of alite-rich Portland cement were stu***d.
研究了礦渣、粉煤灰和燒頁岩單摻及複摻對高阿利特水泥凝結時間、抗壓強度、電阻率、水化産物組成及微觀結構的影響。
By using the gel property of FGD -gypsum, mixing it with waste material from thermal power plant in a certain proportion can generate a component similar to hydrated product of cement.
利用脫硫石膏的膠凝性能，将之與火電廠廢棄物按一定比例混合後，能産生與水泥水化産物相似的成分。
The study also shows that calcium silicate hydrate gel, analcite and hydrated calcium aluminosilicate are the major hydration products of the cement.
堿磷渣水泥的主要水化産物是水化矽酸鈣、方沸石、水化矽鋁酸鈣。
Hydrated Cement（水化水泥）指水泥與水發生化學反應後形成的固态産物，是混凝土硬化的核心物質基礎。該過程稱為“水化反應”，其本質是水泥熟料中的矽酸鹽礦物（如C₃S、C₂S）與水分結合，生成水化矽酸鈣凝膠（C-S-H）和氫氧化鈣（Ca(OH)₂）等化合物。
從材料科學角度分析，水化過程分為三個階段：
國際權威機構美國混凝土學會（ACI）指出，水化程度直接影響混凝土的28天抗壓強度與耐久性指标（來源：ACI 318建築規範）。清華大學土木工程系實驗數據顯示，完全水化的水泥漿體孔隙率可降低至15%以下（來源：清華大學建築材料國家重點實驗室年度報告）。
該術語常與“未水化水泥顆粒”形成對比，後者殘留在混凝土中可能引發後期膨脹開裂。英國利茲大學材料學院研究發現，控制水灰比在0.4-0.6區間可優化水化效率（來源：Cement and Concrete Research期刊第92卷）。
hydrated cement 是建築材料領域中的專業術語，其含義和用法如下：
hydrated cement 指水化水泥，即水泥與水發生化學反應後的産物。這一過程被稱為“水化反應”（hydration），是水泥硬化和形成強度的關鍵步驟。
hydrated（形容詞）：
cement（名詞）：
在工程中，hydrated cement 是硬化水泥漿體的核心成分。水泥中的矽酸三鈣（C₃S）與水反應生成水化矽酸鈣凝膠（C-S-H）和氫氧化鈣（Ca(OH)₂），其反應可簡化為： $$ C_3S + H_2O → C-S-H + Ca(OH)_2 $$ 這一過程賦予混凝土強度和耐久性。
如需更詳細的化學反應機制或工程案例，建議查閱建築材料專業文獻。