[機] 電渣焊
The procedure using anneal instead of normalizing will improve the productive efficiency of electroslag welding joint.
用退火代替正火後的電渣焊工藝可大大提高生産效率。
The re-bar end used for electroslag welding should be straight, flat and clean free of U-shaped, bruising, concave and convex, bending or distorted deformations.
電渣壓力焊焊接使用的鋼筋端頭應平直、幹淨，不得有馬蹄形、壓扁、凸凹不平、彎曲扭曲等嚴重變形。
Within 200mm area of re-bar end surface, it should be free of rust, oil dirt, concrete slurry etc. The contaminated re-bar should be cleaned for electroslag welding.
鋼筋端部200 mm範圍不應有鏽蝕、油污、混凝土漿等污染，受污染的鋼筋應清理幹淨後才能進行電渣壓力焊焊接。
According to the specification of equipment, the hardware and PLC application software have been designed. This control system has been used in double wires electroslag welding.
根據設備的技術要求設計了系統硬件和PLC應用軟件，該系統已用于自制雙絲電渣焊設備。
Nickel rod needs to be lengthen by argon arc welding before the electroslag refinements, large welding parameters are needed to assure the sufficient penetration.
金屬鎳在電渣精煉前需用氩弧焊焊接接長，為保證焊接接頭具有足夠熔深，需要大參數進行焊接。
電渣焊（Electroslag Welding，簡稱ESW）是一種利用電流通過導電熔渣産生的電阻熱進行焊接的工藝。其原理是将被焊工件垂直放置，在間隙中填充焊劑和焊絲，通過電流使焊劑熔化成導電熔渣池。熔渣的電阻熱持續熔化焊絲和母材邊緣，熔融金屬在銅制水冷滑塊引導下凝固，形成緻密焊縫。該技術適用于40-500毫米厚度的碳鋼、低合金鋼等材料的垂直焊接，具有單道焊透能力強、效率高的特點（來源：美國焊接學會《焊接手冊》）。
電渣焊在重型機械制造領域應用廣泛，例如三峽水電站700兆瓦水輪機轉輪的制造中就采用了該技術，成功實現了500兆帕級高強度鋼闆的可靠連接（來源：中國機械工程學會《機械工程學報》）。國際标準化組織ISO 4063:2023标準将其歸類為第72類焊接工藝，規範了其在壓力容器制造中的工藝參數（來源：ISO官網）。
電渣焊（Electroslag Welding）是一種利用電流通過液态熔渣産生的電阻熱進行焊接的工藝，主要用于焊接厚金屬構件。以下是其核心要點：
基本原理
通過電流在導電熔渣中産生電阻熱，熔化焊絲和母材，形成熔池并逐漸冷卻凝固，實現金屬連接。與電弧焊不同，電渣焊的熱源穩定且集中，適合大厚度材料。
主要類型
應用領域
主要用于焊接厚鋼闆（如橋梁、船舶、壓力容器）和大型鑄鍛件，尤其在建築、重型機械制造中應用廣泛。
工藝特點
局限性
僅適用于垂直或近垂直位置的焊接，且焊後需進行熱處理以消除粗晶組織。
如需進一步了解具體工藝參數或案例，可參考焊接工程手冊或專業文獻。