蠕變斷裂
The results shows that the main reason of stainless steel pipe cracking is that intercrystalline corrosion result in creep rupture.
結果表明，不鏽鋼管”鼓包”狀開裂的主要原因是晶間腐蝕導緻的蠕變斷裂。
The P92 steel is a steel sort being used for main steam pipelines of ultra-supercritical units at present, its creep rupture life has widely drawn close attention.
P 92鋼是目前超超臨界機組主蒸汽管道的應用鋼種，其蠕變斷裂壽命被廣泛關注。
The carburizing damage of HP type ethane cracking tubes after 40000hours of service is analysed using metallographic methods, and the tensile and creep rupture tests are conducted.
對運行了4萬h的HP型乙烷裂解爐管的滲碳損傷進行了金相分析，并測定了爐管的力學性能。
In experimental stu***s the authors considered the behaviour of various metals under constant and variable stresses, stress concentration, influence of way of loading on creep rupture;
在試驗研究中本文考慮了各種金屬在恒應力與變應力下的行為，應力集中，加載方式對蠕變破壞的影響；
The methods of creep test to get both curves of tensile creep rupture load vs time and creep strain vs time are compared. The procedures to extrapolate the two types of creep curves are presented.
比較了獲得拉伸蠕變破壞荷載-時間曲線以及蠕變應變-時間曲線的試驗方法，給出了外推這兩種蠕變曲線數據的處理步驟。
在材料科學與工程領域，"creep+rupture"是描述材料在高溫和持續應力作用下漸進性失效過程的專業術語，可分為兩部分理解：
1. 蠕變（Creep）
指固體材料在低于屈服強度的恒定應力作用下，隨時間的推移發生緩慢塑性變形的現象。該過程具有顯著的溫度依賴性，通常發生在材料熔點溫度的30%-50%以上。根據美國材料試驗協會（ASTM E139）标準，典型蠕變曲線分為三個階段：初始階段的變形速率遞減、穩态階段的恒定速率，以及加速階段的最終斷裂前兆。
2. 斷裂（Rupture）
特指材料在蠕變過程中因微觀缺陷（如孔洞、晶界滑移）的累積而發生的最終分離現象。英國國家物理實驗室（NPL）研究指出，斷裂時間與應力水平呈指數關系，這一規律被廣泛應用于高溫設備壽命預測。
兩者的結合（creep-rupture）完整描述了材料從緩慢變形到突然失效的全過程。例如在燃氣輪機葉片設計中，工程師需依據ASM國際材料信息學會發布的《高溫合金手冊》中蠕變斷裂強度曲線，選擇能夠承受10萬小時以上持續載荷的材料。該現象的研究對航空航天、核反應堆壓力容器等關鍵領域的安全性評估具有決定性作用。
“Creep rupture”是材料科學和工程領域的術語，結合“creep”（蠕變）和“rupture”（斷裂）兩者的特性。以下是詳細解釋：
指材料在長期應力作用（尤其是高溫環境）下，經曆蠕變變形後最終發生斷裂的現象。例如：
在工程中，需通過高溫持久試驗測定材料的蠕變斷裂數據，以确保設備在長期使用中的安全性。
如需更詳細的技術參數或試驗方法，可參考材料力學或高溫工程相關文獻。