[高分子][物] 软化温度，软化点
The thermal stability and Vicat softening temperature of blends rise at certain degree also.
此外，共混物的热稳定性和维卡软化点温度也有一定程度的提高。
The results showed that the Vicat softening temperature and the tensile yield strength were improved with increasement of CPVC content.
结果表明，共混材料的维卡软化温度和拉伸屈服强度随CPVC用量的增加而增加；
In this paper, through orthogonal experiments, the effect of processing parameters on vicat softening temperature and mechanical properties of the PVC alloy have been stu***d.
本文用正交试验研究了加工工艺参数对PVC合金维卡软化温度和力学性能的影响。
Through the use of a radial-based function neural network(RBFNN) an intelligent forecasting model for the blended-coal softening temperature was set up under MATLAB environment.
采用径向基神经网络（RBFNN）在MATLAB环境下建立了混煤软化温度的智能预测模型。
The result showed that the tensile strength property and Vicat softening temperature was increased and notched impact property of PVC/ABS composite was decreased with the glass fiber added.
研究结果表明：随着玻璃纤维添加份数的增加，PVC/ABS合金的拉伸性能和维卡软化温度有不同程度的提高，缺口冲击强度有所下降。
|softening point/sintering temperature;[高分子][物]软化温度，软化点
"软化温度（softening temperature）"是材料科学和工程学中的关键参数，指材料在受热条件下开始失去刚性并发生塑性变形的临界温度值。该温度点对材料加工性能、热稳定性评估具有重要意义，常见于高分子材料、玻璃、金属合金等领域。
在聚合物领域，软化温度通常通过维卡软化温度测试法（Vicat Softening Temperature）测定，标准测试条件依据ASTM D1525或ISO 306，主要反映热塑性材料在特定负荷下的耐热能力。例如聚氯乙烯（PVC）的维卡软化温度约为70-85°C，直接影响其管道制品的热水输送性能。玻璃材料的软化点（Softening Point）则通过ASTM C338标准测定，普通钠钙玻璃的软化温度约为720°C，该参数决定玻璃成型工艺的温度窗口。
该参数受材料微观结构影响显著：高分子材料的分子量分布、交联密度会影响软化行为，如高密度聚乙烯（HDPE）因结晶度高，其软化温度（约120-130°C）明显高于低密度聚乙烯（LDPE）（约80-95°C）。金属材料的软化温度则与再结晶温度相关，例如铅的再结晶温度低于室温，因此在常温下即表现出蠕变特性。
"softening temperature"（软化温度）指材料在受热过程中开始失去刚性并发生软化的临界温度值。具体可分为以下两类解释：
维卡软化温度（Vicat Softening Temperature）
专指热塑性塑料的软化性能测试指标，即在液体传热介质中，材料受1mm²压针施加特定负荷，并以等速升温至压入试样1mm深度时的温度（测试标准如GB/T 1633-2000）。该指标反映材料耐热性，常用于评估工程塑料的高温稳定性（如MPP管材检测）。
广义软化温度
泛指材料从固态向软化状态转变的温度，例如陶瓷烧结过程中颗粒间结合力降低的起始温度。这类软化可能与晶界变化、空隙收缩等物理过程相关，但不同于维卡软化温度的标准化测试条件。
补充说明